고무의 열적 특성
열전도율: 고무는 열전도율이 낮고 열전도율 계수는 두께가 25mm일 때 약 2.2~6.28 W/m2.0K입니다. 우수한 단열재입니다. 고무를 미세다공성 또는 스펀지 상태로 만들면 단열 효과가 더욱 향상되어 열전도율이 0.4~2.{10}} 와트로 감소합니다. 고무 부품은 사용 시 히스테리시스 손실로 인해 발열이 발생할 수 있으므로 방열에 주의하십시오.
Thermal expansion: because there is a large free volume between rubber molecular chains, the internal rotation of its chain segments becomes easier when the temperature rises, which will make its volume larger. The linear expansion coefficient of rubber is about 20 times that of steel. This must be considered in the vulcanization model design of rubber products, because the linear size of rubber products will be 1.2~3.5% smaller than the model. For the same type of rubber, the hardness of the rubber compound and the content of raw rubber also have a greater impact on the shrinkage of the rubber compound. The shrinkage is inversely proportional to the hardness and is proportional to the rubber content. The order of shrinkage of various rubbers in theory is: fluororubber>silicone rubber>butyl rubber>nitrile rubber>neoprene>styrene butadiene rubber>천연 고무. 고무 제품을 저온에서 사용하는 경우 부피 수축의 영향에 특별한 주의를 기울여야 합니다. 예를 들어, 오일씰은 수축으로 인해 누수가 발생하고 고무 및 금속 접합 제품은 수축으로 인해 과도한 응력이 발생하여 조기 손상이 발생합니다.